Evaluation of the Behavior of The Physical and Mechanical Properties of Green Concrete Exposed to Magnesium Sulfate

##plugins.themes.bootstrap3.article.main##

  •   Laura Landa-Ruiz

  •   Hilda Ariza-Figueroa

  •   Griselda Santiago-Hurtado

  •   Victor Moreno-Landeros

  •   Raúl Alberto López Meraz

  •   Rafael Villegas-Apaez

  •   Sabino Márquez-Montero

  •   René Croche

  •   Miguel Angel Baltazar-Zamora

Abstract

In the present research work, four concrete mixtures were designed according to the ACI 211.1 method, the first as a control mixture, with 100% CPC, and the remaining three elaborated with partial replacement of the CPC by combinations of Sugar Cane Bagasse Ash and Silica Fume (SCBA-SF) in 10%, 20% and 30% (Green Concrete). The tests carried out on the four mixtures were physical properties (Slump, Temperature, Density) and mechanical properties as Compressive Strength (F'c) and Modulus of Elasticity, according to the ASTM and ONNCCE standards, the study specimens were exposed in water, as a control medium and a 3.5% solution of MgSO4 as an aggressive medium for a period of 28 days. The results obtained indicate a good performance of the Green Concrete in comparison with the control mixture, in particular the Green Concrete made with 10% and 20% substitution of CPC by SCBA-SF.


Keywords: Green Concrete, Compressive Strength (F'c), Modulus of Elasticity, SCBA-SF, MgSO₄

References

O. Troconis de Rincón et. al., (2016). Reinforced Concrete Durability in Marine Environments DURACON Project: Long-Term Exposure. Corrosion, 72:6, pp. 824-833.

Miguel Angel Baltazar-Zamora, Laura Landa-Ruiz, Yazmin Rivera, René Croche. (2020). Electrochemical Evaluation of Galvanized Steel and AISI 1018 as Reinforcement in a Soil Type MH. European Journal of Engineering Research and Science, 5:3, pp. 259-263.

M. Criado, D.M. Bastidas, S. Fajardo, A. Fernández-Jiménez, J.M. Bastidas. (2011). Corrosion behaviour of a new low-nickel stainless steel embedded in activated fly ash mortars. Cement and Concrete Composites, 33, pp. 644-652.

A. Landa-Gómez et.al., (2018). Correlation of Compression Resistance and Rupture Module of a Concrete of Ratio w/c= 0.50 with the Corrosion Potential, Electrical Resistivity and Ultrasonic Pulse Speed. ECS Transactions. 84, 217-227.

D.M. Bastidas, M. Criado, S. Fajardo, A. La Iglesia, J.M. Bastidas. (2015). Corrosion inhibition mechanism of phosphates for early-age reinforced mortar in the presence of chlorides. Cement and Concrete Composites, 61, pp. 1-6.

G. Santiago-Hurtado, M.A. Baltazar-Zamora, A. Galindo D, J.A. Cabral M, F.H. Estupiñán L., P. Zambrano Robledo, C. Gaona-Tiburcio. (2013). Anticorrosive Efficiency of Primer Applied in Carbon Steel AISI 1018 as Reinforcement in a Soil Type MH. International Journal of Electrochemical Science, 8:6, pp. 8490-8501.

M.K. Yashwanth, B.G. Naresh Kumar, D.S. Sandeep Kumar. (2019). Potential of Bagasse Ash as Alternative Cementitious Material in Recycled Aggregate Concrete. International Journal of Innovative Technology and Exploring Engineering, 8:11, pp. 271-275.

O. Ojeda-Farías, J.M. Mendoza-Rangel, M.A. Baltazar-Zamora. (2018). Influence of sugar cane bagasse ash inclusion on compacting, CBR and unconfined compressive strength of a subgrade granular material. Revista ALCONPAT, 8:2, pp. 194-208.

M.A. Baltazar-Zamora, G. Santiago-Hurtado, V.M. Moreno L, R. Croche B, M. de la Garza, F. Estupiñan L, P. Zambrano R., C. Gaona-Tiburcio. (2016). Electrochemical Behaviour of Galvanized Steel Embedded in Concrete Exposed to Sand Contaminated with NaCl. International Journal of Electrochemical Science, 11:12, pp. 10306-10319.

M.A. Baltazar-Zamora, G. Santiago-Hurtado, C. Gaona-Tiburcio et. al. (2012). Evaluation of the corrosion at early age in reinforced concrete exposed to sulfates. International Journal of Electrochemical Science, 7:1, pp. 588-600.

Miguel Angel Baltazar-Zamora, Sabino Márquez-Montero, Laura Landa-Ruiz, René Croche, Oscar López-Yza. (2020). Effect of the type of curing on the corrosion behavior of concrete exposed to urban and marine environment. European Journal of Engineering Research and Science, 5:1, pp. 91-95.

G. Santiago-Hurtado et. al. (2016). Electrochemical Evaluation of Reinforcement Concrete Exposed to Soil Type SP Contaminated with Sulphates. International Journal of Electrochemical Science, 11:6, pp. 4850-4864.

M.A. Baltazar-Zamora et. al. (2012). Efficiency of Galvanized Steel Embedded in Concrete Previously Contaminated with 2, 3 and 4% of NaCl. International Journal of Electrochemical Science, 7:4, pp. 2997-3007.

Miguel Angel Baltazar-Zamora, José Manuel Mendoza-Rangel, René Croche, Citlalli Gaona-Tiburcio, Cindy Hernández, Luis López, Francisco Olguín, Facundo Almeraya-Calderón. (2019). Corrosion Behavior of Galvanized Steel Embedded in Concrete Exposed to Soil Type MH Contaminated with Chlorides. Frontiers in Materials, 6, pp. 1-12.

A. Landa-Gómez et.al., (2018). Corrosion Behavior 304 and 316 Stainless Steel as Reinforcement in Sustainable Concrete Based on Sugar Cane Bagasse Ash Exposed to Na2SO4. ECS Transactions. 84, pp. 179-188.

M.A. Baltazar-Zamora, D.M. Bastidas, G. Santiago-Hurtado, J.M. Mendoza-Rangel, C. Gaona-Tiburcio, J.M. Bastidas, F. Almeraya-Calderón. (2019). Effect of Silica Fume and Fly Ash Admixtures on the Corrosion Behavior of AISI 304 Embedded in Concrete Exposed in 3.5% NaCl Solution. Materials (Basel), 12:23, pp. 1-13.

G. Santiago-Hurtado et. al. (2016). Electrochemical Evaluation of a Stainless Steel as Reinforcement in Sustainable Concrete Exposed to Chlorides. International Journal of Electrochemical Science, 11:4, pp. 2994-3006.

Miguel Angel Baltazar-Zamora, Hilda Ariza-Figueroa, Laura Landa-Ruiz, and René Croche. (2020). Electrochemical Evaluation of AISI 304 SS and Galvanized Steel in Ternary Ecological Concrete based on Sugar Cane Bagasse Ash and Silica Fume (SCBA-SF) exposed to Na2SO4. European Journal of Engineering Research and Science, 5:3, pp. 353-357.

Hilda A. Ariza-Figueroa et. al. (2020). Corrosion Behavior of AISI 304 Stainless Steel Reinforcements in SCBA-SF Ternary Ecological Concrete Exposed to MgSO4. Materials (Basel), 13:10, pp. 1-16.

Abigail Landa-Sánchez et. al. (2020). Corrosion Behavior of Steel-Reinforced Green Concrete Containing Recycled Coarse Aggregate Additions in Sulfate Media. Materials (Basel), 13:19, pp. 1-22

ACI. Provision of mixtures, normal concrete, heavy and massive ACI 211.1, p. 29. Ed. IMCYC, México (2004).

ASTM C29 / C29M–07–Standard Test Method for Bulk Density (“Unit Weight”) and Voids in 412 Aggregate; ASTM International, West Conshohocken, PA, 2007, www.astm.org.

ASTM C33/C33M–16e1–Standard Specification for Concrete Aggregates; ASTM International, 414 West Conshohocken, PA, 2016, www.astm.org.

ASTM C127–15–Standard Test Method for Relative Density (Specific Gravity) and Absorption of 416 Coarse Aggregate; ASTM International, West Conshohocken, PA, 2015, www.astm.org.

ASTM C128–15–Standard Test Method for Relative Density (Specific Gravity) and Absorption of 418 Fine Aggregate; ASTM International, West Conshohocken, PA, 2015, www.astm.org.

NMX-C-414-ONNCCE 2014: Cementantes Hidráulicos. ONNCCE, S.C.; Mexico 2014.

NMX-C-156-ONNCCE-2010: Determinación del revenimiento en el concreto fresco. ONNCCE S.C., México, (2010).

ASTM C 1064/C1064M–08–Standard Test Method for Temperature of Freshly Mixed Hydraulic-426 Cement Concrete; ASTM International, West Conshohocken, PA, 2008, www.astm.org.

NMX-C-162-ONNCCE-2014: Determinación de la masa unitaria, cálculo del rendimiento y contenido de aire del concreto fresco por el método gravimétrico., ONNCCE S.C., México, (2014).

NMX-C-083-ONNCCE-2014: Determinación de la resistencia a la compresión de especímenes – Método de prueba, ONNCCE S.C., México, (2014).

NMX-C-128-ONNCCE-2013: Determinación del Modulo de Elasticidad Estático y Relación de Poisson, ONNCCE S.C., México, (2013).

Downloads

Download data is not yet available.

##plugins.themes.bootstrap3.article.details##

How to Cite
[1]
Landa-Ruiz, L., Ariza-Figueroa, H., Santiago-Hurtado, G., Moreno-Landeros, V., López Meraz, R.A., Villegas-Apaez, R., Márquez-Montero, S., Croche, R. and Baltazar-Zamora, M.A. 2020. Evaluation of the Behavior of The Physical and Mechanical Properties of Green Concrete Exposed to Magnesium Sulfate. European Journal of Engineering Research and Science. 5, 11 (Nov. 2020), 1353-1356. DOI:https://doi.org/10.24018/ejers.2020.5.11.2241.